Bundan tashkari, boshka kism 12 shisha pogona bilan ?osil kilingan pogonali kismga 124 ega va pogonali kism 124 shisha taglikka kagan tomondan le?imlash orkali shisha taglikka epishtirilgan. 123. Bundan tashkari, birlashtiruvchi kism 121 boshka uchida birlashtiruvchi kismga 121 perpendicular yynalishda chetidan chyzilgan vertical kism 122 va vertical kismning ohirida birlashtiruvchi kism 121 ga sezilarly darazhada parallel ravishda chyzilgan chizikka ega.. 122. Yassi kism 125 kengaitirilgan. Vertical kism 122 11-kismning vertical kism 112. Yani 11-kismning vertical kismi 121 va boshka kismning 12-vertical kismi 122 bir-biriga tegib turadi.
Terminalni oina sirtiga elektr kontakti sifatida kavshirlanganda oina va kashirlash kushimcha materialarini issyklikdan kengayish koieficienti turlicha bulganligi sababli kontakt vakt utishi bilan kucishi mumkin. Bu kamchilikni tuzatishni usullaridan biri kavshirlash materialarini tarkibini tadkikotlar asosida tugri tanlashdir.
Tadkikotlarni natijalaridan maylumki, kavshirlash sifati (degrodatsiyasiga) kullaniladigan flux tartibi va tarkibiga ham boglik. Flux bilan kaita ishlangan maidon 3 dan 20:1 nisbat munosabatida bulishi kerak. Bundan tashkent kavshrlashdan oldin surtilgan flux kavshirlashdan keyin tozalab tashlanmaidi. Kavshirlash natijalarini samaradorligiga kullanilaetgan flux tarkibiga ham boglik.
Kupchilik tadkikotlarni kursatisic kavshirlash kushimcha materiali sirt zichligi mikdori 0.18 dan 1.43 g/cm 2 oralikda yahshi natija beradi. Oina sirtiga terminalni kavshirlash temperaturasi 20-200°From oralikda buladi.
Yahshi natija bergan tadkikotlarda kavshirlash kushimcha materiali Sn-Zn (kalai-rukh) tarkibda Zn ulisha mass 8% ni tashkil etadi.
Misol uchun Sn-Zn soldering iron temperaturasi 260° C eki 320° C bulganda sifatli kavshirlash amalga oshadi. Metal chikish (electrode) 1 mis eki latun elementni oz ichiga oladi. Kavshirlash kushimcha materialini 113 va 123 sirtlarda sirt zichligi 1,18 g/cm 2 ni tashkil etadi.
Kavshirlash technolgiyasini oinaga tasirini aniklash maksadida mahsus ketma ketlikda tazhribadar utkazilgan.
Issyklik davri sinovi ?ar bir namuna uchun tsiklni takrorlash orkali amalga oshirildi, u 30 daka davomida -30° C da saklangan va keyin bir cycle sifatida 30 daka davomida 80° C da saklanadi. Bundan tashkari, tsiklni takrorlash zharaenida shisha taglikdagi yeriklar paydo bylishi bevosita kyz bilan kuzatilgan va yeriklar paydo bylishini kuzatishda yeriklar paydo bylishidan oldin takrorlangan tsiklar sonisoblangan.
2-zhadvalda ushbu ihtironing kavshirlash usuli bilan ishlab chikarilgan namunalar (misollar) va kiesiy misollar uchun isitish davri sinovining natijalari kyrsatilgan. Issyklik davrlari sony 300 dan kam bilgan va shisha tagida yeriklar paido bilgan ?olat "X" bilan, thermal davrlar sony 300 va undan kyp bilgan ?olat "?" bilan kyrsatilgan.
2-zhadvaldan kirinib turibdiki, metal kyrgoshin materiali electrodi latun bilgan kiyoshi misolda, soldering ironing ?arorati 310° C eki 260° C, flux maidoni nisbati 3 dan kam. Birlik uchun kavshirlash kushimcha materiali sirte zichligi 0,14 dan 1,18 g/cm 2 oraligida bilsa, barcha namunalar thermal cyclda 300 martadan kichik bulgan holdayek yerlib ketgan.
Ikkinchi tomondan, metal metal chikish electrodi latun bilgan namunadagi misolda, payalnikning ?arorati 260° C eki 320° C, birlik maidoni uchun kotishma sirte zichligi 1,18 g / cm2, flux maidoni. 4,5, 18 va 20 nisbatlaring ?ar kandayida thermal davrlar sony 300 martadan oshdi va ma?sulot mukammal sifatga ega ekanligi tasdiklandi. Ainiksa, flux maidoni nisbati 20 ga teng bulgan namunali misolda, shisha taglik 3000 With eki undan ortik isitish davrlaridan keyin ?am yerlib ketmaydi va sifati judah yahshi.
Hulosa. Keltirib utilgan takhlilii materiallardan hulosalash mumkinki, avtolarni oynalarini elektr energiyasi orkali kizdirish tizimini tashkil etish buyicha judah kup ilmiy izlanishlar olib borilgan. Bu ilmiy izlanish natijalari fakat ilmiy patentlar orkali mualliflashtirilgan. Ilmiy natijalar ochik ilmiy journalarda elon kilnmagan. Buning sababi, tadkikotlar mavzulari avtovil sanoatiga talukligi va mavzularni fakat hizmat foidalanishi ("chipboard" for service use) grifida bulganligidir.
Ilmiy tadkikotlar takhlili kursatadiki, metal kontaktlarni (terminallarni) but metal materiallarga kavshirlashda anik technologik talablarga etibor karatish lozim. Birinchi navbatda kavshirlash kushimcha materiali tarkibi keltiribulgan tarkibda bulishi, ikkinchidan kavshirlashda kavshirlash maidonini flux bilan kaita ishlash maidoni kashirlash maidonidan kamida 3 marotaba katta bulishi, uchinchidan kavshirlashni anik temperature intervalida amalga oshirilishi kerak.
Literature
1. EP1688284A2 *2005-02-042006-08-09OOO "Automotive Components Holdings"The method of manufacturing a heated windshield
2. JP2009504411A *2005-08-122009-02-05Состав solder
3. WO2012096373A1 *2011-01-142012-07-19ОконОкон Window glass for vehicles and the method of its manufacture
4. US20070037004A1 *2005-08-122007-02-15corporation Antaya technologiimnogolayny solder
5. DE102006019998A1 *2006-04-262007-10-31Few Fahrzeugelektrik Werk Gmbh & Co. The device for soldering contacts on a silver impression of automobile glass contains a base frame, a coordinate table opposite to the frame, and a layer of glass adjusted according to the mass and curvature of the individual glass of the car.
6. EP2408260A1 *2010-07-132012-01-18Saint-Gobain Glass French Glass panel with electrical connection element
7. HU052512T2 *2011-07-042021-05-28Sen-Goben for the manufacture of glass with an electric connecting element
8. WO2019108006A12017-11-302019-06- 06Saint-Gobain Glass Francia device for soldering the terminals on the car window glass and the method of soldering it
9. JP2020015080A *2018-07-272020-01-30 A soldering device
10. CN108356377A *2018-05-152018-08-03 A method for processing the appearance of a lead-acid battery terminal and tools for performing this method.
11. WO2020162354A1 *2019-02-082020-08-13 The glass plate module
12. US10105794B22018-10-23 Method of forming a composition of lead-free solder
13. JP6106801B22017-04-05 Soldering method and automotive glass
14. TV201615854A2016-05-01 Low-temperature high-reliability alloy for solder hierarchy
15. WO2012118203A12012-09-07 for connecting the car window glass to the power supply terminal
16. JP4957246B220.06.2012 Car Window glass
17. JP2016536145A2016-11-24 Bonding with aluminum
18. WO2014021308A12014-02-06 Metal bonding strip and soldering method using it
19. JPH10193169A1998-07-28 Lead-free solder
20. TV202108280A2021-03-01 Flux and solder paste
21. JPH1133776A1999-02-09 Soldering material and electronic part with its use
22. JP3782743B22006-06-07 Solder composition, soldering method and electronic component
23. CA1245475A1988-11-29 Solder compositions, fluxes and methods of application
24. JPH09277082A1997-10-28 Solder paste
25. WO2020031361A12020-02-13 Lead-free solder, solder paste, electronic circuit substrate and electronic control device
26. WO2014142153A12014-09-18pipe and its connection
27. WO2019098169A12019-05-23 Flux, flux core solder and flux coated granules
28. JP7181964B22022-12-01Conducting composition containing solder and a method for manufacturing an electronic substrate
29. JP7137212B22022-09-14 FLUX, SOLDER COMPOSITION AND METHOD OF CONNECTION MANUFACTURE
30. RU2451587C12012-05-27 Solder for soldering aluminum and its alloys
31. WO2007003692A12007-01-11 Method of preparing solder suitable for joining two metal parts, solder and solder use
32. KR101865727B12018-06-08B Lead-free solder
33. US20100147929A12010-06-17 – Metal compounds
34. JP2014146713A2014-08-14 Solder material and soldering method
35. JP2014034050A2014-02-24 METHOD OF MANUFACTURING METAL COUPLING AND TERMINAL BOARD Cu
36. JP2016505312A2014-02-282015-02- 27 Soldering method and car glass